Sebopeho sa motsoako oa 6082 pele le ka mor'a homogenization

1. Motsoako oa motsoako

2. Homogenization Process

390 ℃ x insulation bakeng sa 1.0h + 575 ℃ x insulation bakeng sa 8h, moea o pholileng o matla ho ea ho 200 ℃ ebe o pholile metsi.

3. Sebopeho sa Metallographic

Setšoantšo sa 1 Sebopeho sa Metallographic ea mantlha ea 6082 alloy ingot, e hlophisitsoeng ke Keller reagent, e nang le li-dendrite tse tsoetseng pele hantle.

Setšoantšo sa 2 Metallographic sebopeho sa mantlha sa 6082 alloy ingot, se hlophisitsoeng ke Keller reagent, le sebopeho kamora tharollo e tiileng.

4. Phello ea phekolo ea mocheso oa homogenization mohahong oa alloy

4.1 Joalokaha ho bontšitsoe setšoantšong sa 1, alloy e na le li-dendrites tse tsoetseng pele hantle sebakeng sa cast, 'me ho na le palo e kholo ea marang-rang a marang-rang a se nang tekano methating ea lipula meeding ea lijo-thollo.

4.2 Kaha lintlha tse qhibilihisang tsa likarolo tse fapaneng li fapane ha motsoako o tiisa, ketsahalo ena ea sequential solidification e lebisa ho sebopeho se sa tšoaneng sa solute ka har'a kristale, e bonahalang ka ho khetheha molokong oa palo e kholo ea mekhahlelo ea pula ea marang-rang meeling ea lijo-thollo.

4.3 Ka microstructure ka mor'a phekolo ea homogenization (Setšoantšo sa 2), palo ea mekhahlelo e nang le pula-maliboho meeling ea lijo-thollo e fokotsehile haholo, 'me boholo ba lijo-thollo bo eketseha ka synchronously. Lebaka ke hore ho aroloa ha liathomo ho matlafatsoa tlas'a mocheso o phahameng, ho felisoa ha karohano le ho senyeha ha mekhahlelo e sa tsitsang ho etsahala ka ingot, 'me metsoako ea marang-rang holim'a meeli ea lijo-thollo e qhibiliha ka mokhoa o itseng.

4.4 Ka tlhahlobo ea SEM, joalokaha ho bontšitsoe ho FIG3, likarolo tse fapaneng tsa mohato o fokolang li ile tsa khethoa bakeng sa tlhahlobo ea EDS, ho tiisa hore mohato o neng o le teng ke Al(MnFe)Si phase.

4.5 Nakong ea ho etsoa ha alloy casting, palo e kholo ea Mn-containing precipitation phase e thehoa, 'me karolo ea eona e bolokiloe ka tharollo e tiileng ea supersaturated. Ka mor'a phekolo e phahameng ea mocheso le ea nako e telele ea homogenization, Mn supersaturated ka matrix precipitates ka mokhoa oa Mn-containing compounds, e leng se bonahatsoang e le palo e kholo ea qhalakaneng Mn-e nang le metsoako decomposition particles precipitated ka kristale (Figure 2).

4.6 Kaha karolo ea pula e na le Mn element, e na le botsitso bo botle ba mocheso. Ka ho matlafala ha phallo ea athomo, likaroloana tsa karolo ea Al(MnFe)Si butle-butle li bontša litšobotsi tsa spheroidization.

Fig.3 Al(MnFe)Si phase in 6082 alloy

5. Phello ea tharollo ea botsofali tsamaiso ka thepa ea mechine

Ka mor'a homogenization, netweke precipitated mohato qalong moeling oa lijo-thollo tsa 6082 alloy e qhibiliha, e leng ho ka ntlafatsa akaretsang thepa ea mechine ea sampole. Ka nako e ts'oanang, karolo e tsitsitseng e thibelang mocheso Al(MnFe)Si phase e tsoela pele ho spheroidized, e ka khonang ho phunya hantle. Sena se bonts'a hore ts'ebetso e felletseng ea thepa e tla ntlafatsoa kamora kalafo ea mocheso oa homogenization.

6. Qetello

6.1 The 6082 aluminium alloy ingot e na le li-dendrites tse ntlafalitsoeng hantle le palo e kholo ea mekhahlelo ea pula ea marang-rang e sa lekaneng meeling ea lijo-thollo.

6.2 Ka mor'a phekolo ea homogenization, ho shebella ha microscopic ho ile ha senola hore palo ea mekhahlelo e fokolang e fokotsehile haholo, 'me boholo ba lijo-thollo bo ile ba eketseha ka nako e tšoanang. Ho felisoa ha karohano le ho felisoa ha mekhahlelo e sa leka-lekaneng ho etsahetse ka ingot, 'me metsoako ea marang-rang holim'a meeli ea lijo-thollo e ile ea qhibiliha ka mokhoa o itseng.

6.3 Ha ho etsoa motsoako oa 6082, mohato oa pula oa Al(MnFe)Si oa hlahisoa. Karolo ena ea lipula e na le karolo ea Mn mme e na le botsitso bo botle ba mocheso. Ha ts'ebetso ea homogenization e ntse e tsoela pele, likaroloana tsa mohato oa pula butle-butle li bontša litšobotsi tsa spheroidization. Likaroloana tsena tse nang le Mn li qhalakantsoeng ka mokhoa o ts'oanang 'me li putlama ka har'a kristale.

6.4 Ka mor'a phekolo ea homogenization, ho qhibiliha ha marang-rang a marang-rang a marang-rang ho bontša hore ts'ebetso ea kakaretso ea ingot eohle e ntlafatsoa ka mor'a phekolo ea mocheso oa homogenization.